Toluene diisocyanate manufacturer Knowledge Cashew nut shell oil bio-based modified polyol FX-9007

Cashew nut shell oil bio-based modified polyol FX-9007

Cashew nut shell oil bio-based modified polyol FX-9007

                           

Cashew shell oil bio-based modified polyol FX -9007

Guangzhou Polycarbon provides a series of renewable polyol products for polyurethane formulations.

Cashew shell liquid products exhibit excellent water resistance, low moisture sensitivity, and balanced mechanical strength.

CNSL polyols provide excellent chemical resistance, especially alkali resistance.

Major markets include coatings, adhesives, potting, foam and composites.

Mechanical properties

Recipe

FX -9007/PMDI

= 100/40.3

tensile strength(MPa)

17.3

ShaoDhardnesshardness span>

71

Lap shear strength,(MPa)

10.7

Elongation at break(%)

84

Tg(°C)

23.2

curing conditions

room temperature 7days

Cure Speed ​​

Recipe

FX -9007/PMDI

= 100/40.3

Hard dry(Hours)at 25°C

4.5

Hard dry(Hours)at 5°C

17.3

Hard dry(Hours)at 0°C

22.7

Hydrolytic stability

Polyol samples, and polymerizationMDICure

NCOindex=100)

FX-9007

Lap shear strength (MPa), Control Sample

8.7

80°C/7 After soaking in Tianshui

Lap shear strength (MPa)

6.2

Lap shear strength decreased(%)

28.5

Lap shear strength (MPa), Control Sample

8.7

80°C/7 After soaking in Tianshui

Lap shear strength (MPa)

6.2

Lap shear strength decreased(%)

28.5

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.allhdi.com/archives/1124

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Back to top
Home
E-mail
Products
Search