Product Introduction
Takenate D-110N is a curing agent for aliphatic polyisocyanate synthesized from xylylene diisocyanate (XDI) dissolved in ethyl acetate.
Features
Good weather resistance, yellowing resistance and adhesion;
Aromatic polyisocyanate with better curability than TDI;
It is used in combination with resins containing hydroxyl groups such as polyols and castor oil, and is mainly used in coatings, adhesives, and sealing materials.
Status
|
Appearance |
Light Yellow transparent liquid |
|
ChromaG |
1 Max. |
|
solid content% |
75.0 ±1.0 |
|
Viscosity 25°C, mPa·s |
500 ±400 |
|
NCO content% |
11.5 ±0.5 |
|
FreeXDI Monomer% |
0.5 Max. |
Coating properties*
|
main agent |
Takelac U-27(polyester polyol) |
|
mixing ratio,NCO/OH molar ratio |
1.0 |
|
Acupressure dry,h |
2.4 |
|
active,h |
8 |
|
Adhesion |
100 /100 |
|
Erickson value,mm |
8 |
|
bending resistance,mm |
2 |
|
Impact resistance |
|
|
DuPont method,inch x g x cm |
1 /2 x 1000 x 50 |
|
Pencil Hardness |
H |
*The data provided here are only measured in general use and do not represent the specifications of this product.
Application
It can be used as a coating component for woodworking, furniture, interior decoration, vehicles, paper, plastic coating, outdoor protection, adhesives, sealants, ink adhesives, etc.