Toluene diisocyanate manufacturer Knowledge WH-2935 Water-based PU curing agent for pre-coated film Unseal at ultra-low temperature at 70°C

WH-2935 Water-based PU curing agent for pre-coated film Unseal at ultra-low temperature at 70°C

WH-2935 Water-based PU curing agent for pre-coated film Unseal at ultra-low temperature at 70°C

Model WH-2935

Type Water-based latent isocyanate dispersion (pre-coated film water-based PU curing agent)

Apply Applied to one-component reactive polyurethane dispersion adhesive

Main Features

-Single component low temperature latent reactivity.

-good water-soluble dispersion .

-film formed after drying Possesses latent reactivity.

Product Specifications

physical properties Number

Solid content (%)

40

NCO content

8.0

Appearance

Milky white liquid

PH

8.0-10

Suggestions for use

Due to the specific gravity of curing agent particles Large, so there will be particle precipitation during storage, and it should be redispersed evenly before use. It is recommended to add a suitable thickener to adjust the rheological behavior of the mixture. The recommended dosage is 3-8% of the polymer weight (polymer solids 40-50%).

Save

The curing agent is sensitive to temperature, its processing and storage temperature is recommended not to be higher than 25 degrees, with transportation and The rise in storage temperature will release gas, which will cause the pressure in the container to rise.

Material Safety

Material Safety Data Sheet for this product Sheets are available upon request.

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.allhdi.com/archives/1425

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Back to top
Home
E-mail
Products
Search