Model PF-1010A
Type Water-based two-component polyurethane low-temperature medical positioning board coating
Application Recommended for surface coating of thermoplastic materials such as polycaprolactone that need to be deformed, and surface feel coating on soft materials such as various cloths and plastic films.
Main Features -Self-matting, no need to add matting powder, excellent hand feeling;
- short drying time, good Chemical and water resistance and breathability;
- Very high elongation at break rate, the coating can recover to its original characteristics after cold and heat cycle deformation;
-The coating does not Back stick;
-Good adaptability to human skin , not likely to cause allergic reactions;
- Composite medical material certification standards.
Products Specifications
physical properties |
value |
% of non-volatile components |
30±2 |
Appearance |
milky white viscous liquid |
Viscosity (25oC) |
30±5 |
PH value |
7-9 |
Solvent |
Deionized water |
Elongation (%) |
700 |
Use Recommendation
Wipe the substrate surface clean with solvent, main agent: curing agent: deionized water =20:1:10-20, it is recommended to use a disperser to stir for 10-15 minutes before filtering and spraying. After spraying, enter a 40-degree drying tunnel to bake at a low temperature to dry the surface, and then put it in a 40-degree drying room to mature for more than 24 hours. The operating time after mixing the main agent and curing agent is about 2-3 hours. (Curing Agent WH-1969)