JH-FT foaming agent

JH-FT foaming agent

1. Usage and characteristics

The foaming agent is a white powder. It is a new multi-functional foaming agent made of organic polymer materials and polymerized through scientific technology. Mainly used in foam concrete, foam concrete partition boards, gypsum boards, foam composite silicate thermal insulation materials, foam fly ash ceramsite and other inorganic and organic products that need to reduce bulk density and foam and create pores. In foam Applying this foaming agent to concrete products can reduce the density (weight) of the product without changing the water-cement ratio of the original concrete.

This foaming agent has fast foaming, long foam stabilization time and good stability. It has high strength for foamed concrete and insulation material products. The solution density of the foaming agent is 200-1000g/1, and the bubble size is um-mm.

II. Performance indicators

2% aqueous solution, surface tension 0.02n/m, surface viscosity 1.55Pa·s, foam life 15h.

3. Dosage and usage

1. The foaming agent dosage is 0.8-1.0% of the slurry mass or 0.2-0.4% of the cementing material. Mix 50 times with water to make foam, that is, weigh 1kg of foaming agent, add 50kg of tap water, and use a high-speed beater to beat the aqueous solution with foaming agent into fine foam (until water is no longer visible). Add the fine foam (without water) to the slurry for making the product to reduce the bulk density of the product by 1/2. The added amount is determined based on the bulk density of the product.

2. As a foaming agent, it is required to reduce the dry bulk weight of the product without reducing the strength of the product. After the product is hardened, there will be no shrinkage and no impact on the early strength and later strength. It will also affect the adhesion and shear strength of the product. The shear strength is not reduced. In the experiment, cement perlite concrete was selected. Without changing the original formula ratio and water-cement ratio, 0.8% foaming agent was added to the slurry, and foaming began under mechanical stirring. The fluidity of foam concrete immediately increases. After achieving the self-leveling effect, pour the concrete mold (70.7m×70.7m×70.7m) into a mold and maintain it for 3 days at 21°C and a relative humidity of 85%. After demoulding, it will be cured naturally for 4 weeks. The results are listed as follows:

Performance of adding 0.4% foaming agent to cement perlite concrete slurry

Name

Dry density (kg/m³)

Compressive failure strength (Mpa)

Water absorption (%)

Surface plastering test

0.4% hydrophobic foaming agent concrete

880

2.4

5

Plain directly

Cement perlite concrete

1160

2.6

38

Stretched and plastered

Note: 1. The compressive failure load value is the average value of 3 times.

2. After soaking the sample with water for 4 hours, take it out and dry the surface, weigh it and calculate the water yield. .

From the table, it can be seen that the bulk density of concrete has been reduced, but the compressive strength has not been reduced, and the hydrophobicity has been improved. And it can be plastered directly, which simplifies the construction process.

IV. , Storage and Packaging

This product should be protected from moisture and sun, and stored in a dry and ventilated place. Each bag is packed in 10kg and has a shelf life of two years.</p

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.allhdi.com/archives/18278

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Back to top
Home
E-mail
Products
Search