Tile adhesive

Tile adhesive

1. Product introduction:

This product is a high-quality environmentally friendly polymer cement-based composite material. It is a powdery flexible bonding material made of high-quality quartz sand and cement as aggregates, redispersible polymer powder imported from Germany and mixed with a variety of additives. The mortar has a certain degree of flexibility and can be safely released A certain degree of alternating load (internal and external stress) can fundamentally solve the problems of cracking, hollowing, falling off and leakage in building decoration. Add water and stir to use.

It has the characteristics of simple operation, convenient construction, good water retention, high bonding strength, good workability, long adjustment time, and no tiles falling. It has good water resistance, temperature resistance, waterproof and impermeability, freeze-thaw resistance, cold and heat rapid degeneration resistance, good anti-aging properties and long-term durability.

2. Product application: Choose different models suitable for the adhesion of interior and exterior wall tiles, facing tiles, floor tiles, partition boards, marble, granite, copper tiles, floor tiles, thunder tiles, ceramics and other decorative materials. Knot.

3. Implementation standards: JG158-2004,

4. Reference dosage: 3-5kg/㎡

5. Construction points:

1. Base treatment: Clean the oil, dust, concrete curing agent, release agent and other loose objects on the surface of the base. When the tensile strength of the base layer is less than the bonding strength of the exterior wall facing bricks, reinforcement must be carried out to ensure it is strong and smooth.

2. Prepare the adhesive: water: tile adhesive = 1:4 (weight ratio). Mechanically stir the tile adhesive according to the above ratio for 3-5 minutes (or stir evenly by hand), and adjust When the consistency is suitable for construction, let it sit for 5 minutes and stir again to start construction.

3. Paste the tiles: Apply the evenly mixed flexible tile adhesive on the base layer with a toothed trowel. The mortar thickness is 3mm-5mm (the actual thickness depends on the material of the bricks), and then use The tooth surface of the toothed trowel scrapes out concave and convex grooves, and then the tiles or flake stones are pasted and pressed flat. The tiles can be straightened within 20 minutes.

It can also be pasted using the traditional bonding method. Apply evenly stirred flexible tile adhesive on the back of the ceramic tile or flake stone, paste it piece by piece, and compact it flatly. The construction thickness is 3-5mm is suitable, and the tiles can be straightened within 20 minutes.

For bricks with larger thickness and mass, the adhesive thickness is 5-7mm. The setting time is related to factors such as temperature, dryness and humidity. Generally, the initial setting time is 4 hours and the final setting time is 24 hours. The adjusted adhesive should be used up within 5-6 hours. 24 hours after the ceramic tile or flake stone is pasted, caulking agent can be used for caulking.

4. Notes: The construction temperature is above 5℃; outdoor construction is prohibited when it rains; it is prohibited to add sand, cement and other additives without permission.

item

Unit

Indicators

The state of glue in the container

Even after stirring, no lumps

Time interval when the tensile bond strength reaches 0.17Mpa

Outset time

min

Not less than 10

Adjust time

min

Greater than 5

Tensile bond strength

Mpa

≥0.90

Collapse ratio

≤3.0

Compression Shear Strength

Original strength

Mpa

≥0.80

Temperature resistant for 7 days (d)

%

The intensity ratio is not less than 70

Water resistant for 7 days (d)

%

The intensity ratio is not less than 70

Resistant to freezing and thawing 25 times

%

The intensity ratio is not less than 70

Linear shrinkage

%

≤ 3.0

6. Packing: 50kg/bag.

-TOP: 0px" valign="center" width="97">

Temperature resistant for 7 days (d)

%

Intensity ratio is not less than 70

Water resistant for 7 days (d)

%

The intensity ratio is not less than 70

Resistant to freezing and thawing 25 times

%

The intensity ratio is not less than 70

Linear shrinkage

%

≤3.0

6. Packing: 50kg/bag. </p

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.allhdi.com/archives/18639

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Back to top
Home
E-mail
Products
Search