Toluene diisocyanate manufacturer Knowledge Asahi Kasei Duranate® standard curing agent series TPA-100 /90SB, TKA-100 /90SB, 22A-75PX…

Asahi Kasei Duranate® standard curing agent series TPA-100 /90SB, TKA-100 /90SB, 22A-75PX…

                           

Size 22A-75PX TKA-75B TPA-90SB TKA-90SB TPA-100 TKA-100
Type Standard Standard Standard
Ingredient biuret trimer trimer trimer
Solid content (wt%) 75 75 90 90 100 100
NCO%(wt%) 16.5 16.5 20.9 19.5 23.1 21.8
Free NCO content <0.5% <0.5% <0.5% <0.5% <0.5% <0.5%
Viscosity (mpa.s. 25℃) 250 200 250-500 550~600 1400 2670
Solvent PMA xylene butyl acetate 100#ethyl acetate butyl acetate —D12 —D12
Features High NCO content, weather resistance, quick drying High NCO content, weather resistance, quick drying High NCO content, weather resistance, quick drying
Dryness (hr20℃) 35 25 30 25 30 25
Gel composition ratio 16 hours 48 75 62 75 62 75
1 day 67 87 77 87 77 87
7 days 95 95 95 95 95 95
hardness HB HB F HB F HB
Adhesion steel plate Good Good Good Good Good Good
anti-rust steel plate Good Good Good Good Good Good
Aluminum plate Good Good Normal Good Normal Good
polyamide Good Good Good Good Good Good
polycarbonate Good Good Good Good Good Good
ABS Good Good Good Good Good Good
bending resistance 2φ mandrel Good Good Good Good Good Good
Impact 1/4-500g 30cm 30cm 30cm
Impact 1/4-1000g >50cm >50cm >50cm
Water resistance Good Good Good Good Good Good
gasoline resistance Good Good Good Good Good Good
Chemical Resistance 10% hydrochloric acid Good Good Good Good Good Good
10% sulfuric acid Good Good Good Good Good Good
10% Sodium Hydroxide Good Good Good Good Good Good
Weatherability acryl Good Excellent Excellent Excellent Excellent Excellent
fluorine Excellent Excellent Excellent Excellent Excellent
purpose Used to produce polyurethane coatings with excellent weather resistance

60 degree gloss retention

Color difference

NCO reaction rate of coating film (take 24A-100 as an example)

Asahi Kasei product address: https://www.akcpc.jp/en/duranate/hyoujyun.html

x”>good Good Good Good Good Good Chemical Resistance 10% hydrochloric acid Good Good Good Good Good Good 10% sulfuric acid Good Good Good Good Good Good 10% Sodium Hydroxide Good Good Good Good Good Good Weatherability acryl Good Excellent Excellent Excellent Excellent Excellent fluorine Excellent Excellent Excellent Excellent Excellent purpose Used to produce polyurethane coatings with excellent weather resistance

60 degree gloss retention

Color difference

NCO reaction rate of coating film (take 24A-100 as an example)

Asahi Kasei product address: https://www.akcpc.jp/en/duranate/hyoujyun.html

This article is from the Internet, does not represent the position of Toluene diisocyanate reproduced please specify the source.https://www.allhdi.com/archives/935

author:

Previous article
Next article
Contact Us

Contact us

+86 - 152 2121 6908

Online consultation: QQ交谈

E-mail: sales@newtopchem.com

Working hours: Monday to Friday, 9:00-17:30, closed on holidays
Follow wechat
Scan wechat and follow us

Scan wechat and follow us

Back to top
Home
E-mail
Products
Search